FILARC KV5L
SMAW
Welding current, A
DC+
|
      |
| Classifications | Approvals | Typical all weld metal composition | Typical properties all weld metal | | SFA/AWS A5.5 | | E7015-B2L | | EN 1599 | | ECrMo1L B 42 H5 | | ISO 3580 | | E 1 Cr Mo LB 20 |
| | BV | UP +500degC | |
| CL | | |
| DS | EN 1599 | |
| SS | EN 1599 | |
| UDT | DIN 8575 | |
| VdTÜV | | |
| | C | <0,05 | | Si | <0,5 | | Mn | 0,7 | | Cr | 1,2 | | Mo | 0,6 |
| Recovery
100%
Yield stress, MPa
>390
Tensile strength, MPa
>520
Elongation, %
>20
Elongation, %
>20
| Charpy V | | Test temps, °C | Impact values, J | | +20 | >47 |
|
| Diameter, mm | 2,5 | 3,2 | 4,0 | 5,0 | 6,0 | | Length, mm | 350 | 350 | 350 | 450 | 450 | | Arc voltage, V | 24 | 24 | 24 | 24 | 24 | | Welding current, A | 65-95 | 90-130 | 125-165 | 190-220 | 240-290 | | N. Kg weld metal/kg electrodes | 0,59 | 0,56 | 0,59 | 0,6 | 0,67 | | B. No. of electrodes/kg weld metal | 76,9 | 50,0 | 33,3 | 16,9 | 10,8 | | H. Kg weld metal/hour arc time | 0,7 | 1,0 | 1,3 | 2,2 | 2,9 | | T. Burn-off time, secs/electrode | 63 | 70 | 80 | 98 | 116 |
|
|