OK 76.35
SMAW
Welding current, A
DC(+ -)
|
      |
| Classifications | Approvals | Typical all weld metal composition | Typical properties all weld metal | | SFA/AWS A5.5 | | E8015-B6 | | EN 1599 | | E CrMo5 B 42 H5 |
| | | C | 0,08 | | Si | 0,4 | | Mn | 0,8 | | Cr | 5,0 | | Mo | 0,6 |
| Redrying temperature, °C
350
Redrying time, hours
2
Recovery
115%
Yield stress, MPa
>460
Tensile strength, MPa
>550
Elongation, %
>19
Elongation, %
>19
| Charpy V | | Test temps, °C | Impact values, J | | +20 | >47 |
|
| Diameter, mm | 2,0 | 2,5 | 3,2 | 4,0 | 5,0 | | Length, mm | 300 | 300 | 350 | 450 | 450 | | Arc voltage, V | 23 | 23 | 24 | 24 | 24 | | Welding current, A | 50-70 | 65-95 | 90-130 | 125-165 | 190-220 | | N. Kg weld metal/kg electrodes | 0,57 | 0,57 | 0,56 | 0,58 | 0,59 | | B. No. of electrodes/kg weld metal | 139,0 | 76,9 | 50,0 | 33,3 | 16,9 | | H. Kg weld metal/hour arc time | 0,49 | 0,7 | 1,0 | 1,3 | 2,2 | | T. Burn-off time, secs/electrode | 53 | 63 | 70 | 80 | 98 |
|
|