OK 50.10
SMAW


Welding current, A
AC, DC+ OCV 70 V


ClassificationsApprovalsTypical all weld metal compositionTypical properties all weld metal
SFA/AWS A5.1
E6013
CSN 05 5010
E 46.95
DIN 1913
E 43 42 AR 7
EN 499
E 38 2 A 12
ISO 2560
E 43 4 AR 24
ABS3
BV3
DNV3
DSEN 499
GL3
LR3
SSEN 499
C<0,12
Si0,2
Mn0,5
Redrying temperature, °C
150
Redrying time, hours
3
Recovery
100%
Yield stress, MPa
430
Tensile strength, MPa
500
Elongation, %
25
Elongation, %
25
Charpy V
Test temps, °CImpact values, J
-2058
-30>28

Diameter, mm2,53,24,05,0
Length, mm 350 450 450 450
Arc voltage, V - 25 26 27
Welding current, A 75-110 90-150 140-190 170-250
N. Kg weld metal/kg electrodes - 0,60 0,64 0,63
B. No. of electrodes/kg weld metal - 37,0 24,0 16,0
H. Kg weld metal/hour arc time - 1,5 2,1 3,3
T. Burn-off time, secs/electrode - 65 71 69

 