FILARC 36S
SMAW
Welding current, A
DC+(-), AC OCV 70 V
|
      |
| Classifications | Approvals | Typical all weld metal composition | Typical properties all weld metal | | SFA/AWS A5.1 | | E7016 | | EN ISO 2560-A | | E 42 2 B 12 H10 |
| | BV | 3Y HH | |
| DB | 10.105.05 | |
| DNV | 3 YH10 | |
| GL | 3YH10 | |
| VdTÜV | 01007 | |
| CE | EN 13479 | |
| | C | 0,8 | | Si | 0,7 | | Mn | 0,9 | | P | ³0,03 | | S | ³0,03 | | Dia | | | 2,5 | | | mm: | | | Si | 0,5 | | Mn | 1,2 |
| Recovery
100%
Yield stress, MPa
>420
Tensile strength, MPa
<590
Elongation, %
26
Elongation, %
26
| Charpy V | | Test temps, °C | Impact values, J | | -20 | >54 | | -30 | >28 |
|
| Diameter, mm | 2,5 | 3,2 | 3,2 | 4,0 | 4,0 | 5,0 | | Length, mm | 350 | 350 | 450 | 350 | 450 | 450 | | Arc voltage, V | 22 | 23 | 23 | 23 | 23 | 23 | | Welding current, A | 55-85 | 85-140 | 85-130 | 110-180 | 110-170 | 180-240 | | N. Kg weld metal/kg electrodes | 0,58 | 0,60 | 0,63 | 0,63 | 0,63 | 0,63 | | B. No. of electrodes/kg weld metal | 90,0 | 47,6 | 35,3 | 32,4 | 25,2 | 15,9 | | H. Kg weld metal/hour arc time | 0,8 | 1,1 | 1,1 | 1,6 | 1,6 | 2,4 | | T. Burn-off time, secs/electrode | 50 | 65 | 88 | 75 | 96 | 95 |
|
|