FILARC 36S
SMAW


Welding current, A
DC+(-), AC OCV 70 V


ClassificationsApprovalsTypical all weld metal compositionTypical properties all weld metal
SFA/AWS A5.1
E7016
EN ISO 2560-A
E 42 2 B 12 H10
BV3Y HH
DB10.105.05
DNV3 YH10
GL3YH10
VdTÜV01007
CE EN 13479
C0,8
Si0,7
Mn0,9
P³0,03
S³0,03
Dia
2,5
mm:
Si0,5
Mn1,2
Recovery
100%
Yield stress, MPa
>420
Tensile strength, MPa
<590
Elongation, %
26
Elongation, %
26
Charpy V
Test temps, °CImpact values, J
-20>54
-30>28

Diameter, mm2,53,23,24,04,05,0
Length, mm 350 350 450 350 450 450
Arc voltage, V 22 23 23 23 23 23
Welding current, A 55-85 85-140 85-130 110-180 110-170 180-240
N. Kg weld metal/kg electrodes 0,58 0,60 0,63 0,63 0,63 0,63
B. No. of electrodes/kg weld metal 90,0 47,6 35,3 32,4 25,2 15,9
H. Kg weld metal/hour arc time 0,8 1,1 1,1 1,6 1,6 2,4
T. Burn-off time, secs/electrode 50 65 88 75 96 95

 