FILARC 98S
SMAW
Welding current, A
DC+ -, AC OCV 65 V
|
      |
| Classifications | Approvals | Typical all weld metal composition | Typical properties all weld metal | | SFA/AWS A5.5 | | E9018-G | | EN 757 | | E 55 6 Mn1NiMo B T 32 H5 |
| | | C | 0,06 | | Si | 0,4 | | Mn | 1,8 | | Ni | 0,8 | | Mo | 0,5 |
| Recovery
110%
Yield stress, MPa
>550
Tensile strength, MPa
>660
Elongation, %
>24
Elongation, %
>24
| Charpy V | | Test temps, °C | Impact values, J | | -40 | >80 | | -51 | >60 | | -60 | >40 |
|
| Diameter, mm | 2,5 | 3,2 | 4,0 | | Length, mm | 350 | 350 | 450 | | Arc voltage, V | 24,4 | 23,3 | 24,0 | | Welding current, A | 55-85 | 80-140 | 120-180 | | N. Kg weld metal/kg electrodes | 0,60 | 0,55 | 0,60 | | B. No. of electrodes/kg weld metal | 83,3 | 56,6 | 24,4 | | H. Kg weld metal/hour arc time | 0,72 | 0,94 | 1,43 | | T. Burn-off time, secs/electrode | 60 | 68 | 103 |
|
|