FILARC BM310Mo-L
SMAW
Welding current, A
DC+
|
      |
| Classifications | Approvals | Typical all weld metal composition | Typical properties all weld metal | | EN 1600 | | E 25 22 2 N L R 1 2 | | SFA/AWS A5.4 | | (E310Mo-16) |
| | | C | <0,04 | | Si | <0,5 | | Mn | 4,3 | | Cr | 25,0 | | Ni | 22,0 | | Mo | 2,2 | | Cu | <0,3 | | N | 0,15 |
| Redrying temperature, °C
200
Redrying time, hours
2
Yield stress, MPa
442
Tensile strength, MPa
623
Elongation, %
34
Elongation, %
34
Ferrite content
FN 0
| Charpy V | | Test temps, °C | Impact values, J | | +20 | 54 | | |
|
| Diameter, mm | 2,5 | 3,2 | 4,0 | | Length, mm | 300 | 350 | 350 | | Arc voltage, V | 24 | 24 | 25 | | Welding current, A | 55-70 | 70-100 | 100-140 | | N. Kg weld metal/kg electrodes | 0,72 | 0,56 | 0,55 | | B. No. of electrodes/kg weld metal | 77 | 50 | 33 | | H. Kg weld metal/hour arc time | 0,9 | 1,1 | 1,7 | | T. Burn-off time, secs/electrode | 52 | 62 | 62 |
|
|