FILARC BM310Mo-L
SMAW


Welding current, A
DC+


ClassificationsApprovalsTypical all weld metal compositionTypical properties all weld metal
EN 1600
E 25 22 2 N L R 1 2
SFA/AWS A5.4
(E310Mo-16)
StamicarboUreaplants
C<0,04
Si<0,5
Mn4,3
Cr25,0
Ni22,0
Mo2,2
Cu<0,3
N0,15
Redrying temperature, C
200
Redrying time, hours
2
Yield stress, MPa
442
Tensile strength, MPa
623
Elongation, %
34
Elongation, %
34
Ferrite content
FN 0
Charpy V
Test temps, CImpact values, J
+2054

Diameter, mm2,53,24,0
Length, mm 300 350 350
Arc voltage, V 24 24 25
Welding current, A 55-70 70-100 100-140
N. Kg weld metal/kg electrodes 0,72 0,56 0,55
B. No. of electrodes/kg weld metal 77 50 33
H. Kg weld metal/hour arc time 0,9 1,1 1,7
T. Burn-off time, secs/electrode 52 62 62

 