FILARC 35S
SMAW


Welding current, A
DC+(-), AC OCV 65 V


ClassificationsApprovalsTypical all weld metal compositionTypical properties all weld metal
SFA/AWS A5.1
E7018-1
EN ISO 2560-A
E 42 4 B 32 H5
ABS3H10, 3Y
DB10.105.02
LR3, 3Y H15
VdTÜV00658
CEEN 13479
C0,06
Si0,4
Mn1,1
P³0,03
S³0,02
Recovery
120%
Yield stress, MPa
>420
Tensile strength, MPa
510-600
Elongation, %
>26
Elongation, %
>26
Charpy V
Test temps, °CImpact values, J
-20>100
-40>50
-46>27

Diameter, mm2,02,56,02,53,23,24,05,0
Length, mm 300 300 450 350 350 450 450 450
Arc voltage, V 26 24 22 22 23 23 23 23
Welding current, A 50-80 70-100 240-290 70-100 90-150 90-140 110-170 160-260
N. Kg weld metal/kg electrodes 0,59 128 0,68 0,58 0,63 0,63 0,66 0,68
B. No. of electrodes/kg weld metal 132 80 14 59 43,5 30 24,0 14,2
H. Kg weld metal/hour arc time 0,6 0,6 2,2 1,0 1,29 1,4 1,67 2,62
T. Burn-off time, secs/electrode 43 50 114 57 60 80 95 100
Deposition rate kg weld metal/hour - - - - 1,4 1,4 1,6 2,6

 