FILARC PZ6104
FCAW
Welding current, A
DC+-
|
 |
| Classifications | Approvals | Typical all weld metal composition | Typical properties all weld metal | | EN 758 | | T 42 5 Z M M 2 H5 | | SFA/AWS A5.18 | | E70C-GM H4 |
| | ABS | 3SA, 3YSA | |
| DB | 42.105.11 | |
| DNV | IV YMS (H5) (M21) | |
| LR | 3S 3YS (H15) | |
| VdTÜV | 05477 | |
| CE | EN 14379 | |
| | C | 0,05 | | Si | 0,55 | | Mn | 1,4 | | Ni | 0,825 | | P | 0,025 | | S | 0,025 | | Cr | 0,2 | | Mo | 0,2 | | V | 0,08 | | Nb | 0,05 | | Cu | 0,3 |
| Yield stress, MPa
>420
Tensile strength, MPa
520-620
Elongation, %
22
Elongation, %
22
| Charpy V | | Test temps, °C | Impact values, J | | -40 | >54 | | -50 | >47 |
|
| Diameter, mm | 1,2 | 1,6 | | Arc voltage, V | 21-35 | 17-34 | | Welding current, A | 150-350 | 150-450 | | H. Kg weld metal/hour arc time | 2,1-9,0 | 2,1-9,6 | | Wire feed, m/min | 5,0-21,3 | 2,7-12,3 |
|
|