OK 63.35
SMAW
Welding current, A
DC+
|
      |
| Classifications | Approvals | Typical all weld metal composition | Typical properties all weld metal | | EN 1600 | | E 19 12 3 L B 2 2 | | SFA/AWS A5.4 | | E316L-15 | | Werkstoff Nr. | | 1.4430 |
| | ABS | Stainless | |
| DNV | 316L | |
| VdTÜV | 04815 | |
| CE | EN 13479 | |
| | C | <0,04 | | Si | 0,5 | | Mn | 1,7 | | Cr | 18,5 | | Ni | 12,0 | | Mo | 2,8 | | Cu | <0,3 |
| Redrying temperature, °C
200
Redrying time, hours
2
Recovery
110
Yield stress, MPa
430
Tensile strength, MPa
560
Elongation, %
40
Elongation, %
40
Ferrite content
FN 3-8
| Charpy V | | Test temps, °C | Impact values, J | | +20 | 95 | | -60 | 75 | | -120 | 60 | | -196 | 35 |
|
| Diameter, mm | 2,5 | 3,2 | 4,0 | 5,0 | | Length, mm | 300 | 350 | 350 | 350 | | Arc voltage, V | 24 | 24 | 24 | 24 | | Welding current, A | 55-85 | 80-120 | 80-180 | 150-200 | | N. Kg weld metal/kg electrodes | 0,63 | 0,63 | 0,62 | 0,62 | | B. No. of electrodes/kg weld metal | 91 | 47 | 32 | 20 | | H. Kg weld metal/hour arc time | 0,9 | 1,3 | 1,8 | 2,6 | | T. Burn-off time, secs/electrode | 42 | 58 | 63 | 68 |
|
|