OK 63.35
SMAW


Welding current, A
DC+


ClassificationsApprovalsTypical all weld metal compositionTypical properties all weld metal
EN 1600
E 19 12 3 L B 2 2
SFA/AWS A5.4
E316L-15
Werkstoff Nr.
1.4430
ABSStainless
DNV316L
VdTV04815
CEEN 13479
C<0,04
Si0,5
Mn1,7
Cr18,5
Ni12,0
Mo2,8
Cu<0,3
Redrying temperature, C
200
Redrying time, hours
2
Recovery
110
Yield stress, MPa
430
Tensile strength, MPa
560
Elongation, %
40
Elongation, %
40
Ferrite content
FN 3-8
Charpy V
Test temps, CImpact values, J
+2095
-6075
-12060
-19635

Diameter, mm2,53,24,05,0
Length, mm 300 350 350 350
Arc voltage, V 24 24 24 24
Welding current, A 55-85 80-120 80-180 150-200
N. Kg weld metal/kg electrodes 0,63 0,63 0,62 0,62
B. No. of electrodes/kg weld metal 91 47 32 20
H. Kg weld metal/hour arc time 0,9 1,3 1,8 2,6
T. Burn-off time, secs/electrode 42 58 63 68

 