OK Autrod 13.31
GMAW
Welding current, A
DC+
|
 |
| Classifications | Approvals | Typical all weld metal composition | Typical properties all weld metal | | SFA/AWS A5.28 | | ER110S-G | | EN 12534 | | G Mn4Ni2CrMo |
| | | C | 0,1 | | Si | 0,8 | | Mn | 1,9 | | Cr | 0,4 | | Ni | 2,1 | | Mo | 0,6 | | Cu | <0,3 | | Wire composition |
| Yield stress, MPa
850
Tensile strength, MPa
890
Elongation, %
18
Elongation, %
18
| Charpy V | | Test temps, °C | Impact values, J | | 0 | 70 | | -20 | 60 | | -30 | 50 |
|
| Diameter, mm | 0,8 | 1,0 | 1,2 | 1,6 | | Arc voltage, V | 16-22 | 18-28 | 20-33 | 26-38 | | Welding current, A | 40-170 | 80-280 | 120-350 | 225-480 | | H. Kg weld metal/hour arc time | 0,4-2,6 | 1,0-5,4 | 1,5-6,6 | 3,3-0 | | Wire feed, m/min | 2,0-10,8 | 2,7-14,7 | 2,7-12,4 | 3,1-8,1 |
|
|