OK 48.04
SMAW
Welding current, A
AC, DC+(-) OCV 65 V
|
 |
| Classifications | Approvals | Typical all weld metal composition | Typical properties all weld metal | | SFA/AWS A5.1 | | E7018 | | EN ISO 2560-A | | E 42 4 B 32 H5 |
| | ABS | 3H5, 3Y | |
| BV | 3YHH | |
| DB | 10.039.34 | |
| DNV | 3 YH10 | |
| GL | 3YH10 | |
| LR | 3, 3YH15 | |
| PRS | 3YH10 | |
| RS | 3YHH | |
| Sepros | UNA 409819 | |
| VdTÜV | 00050 | |
| CE | EN 13479 | |
| | C | 0,06 | | Si | 0,5 | | Mn | 1,1 | | P | ³0,03 | | S | ³0,03 |
| Redrying temperature, °C
350
Redrying time, hours
2
Recovery
125%
Yield stress, MPa
480
Tensile strength, MPa
560
Elongation, %
30
Elongation, %
30
| Charpy V | | Test temps, °C | Impact values, J | | -20 | 150 | | -40 | 100 |
|
| Diameter, mm | 2,0 | 2,5 | 3,2 | 3,2 | 4,0 | 5,0 | 6,0 | | Length, mm | 300 | 350 | 350 | 450 | 450 | 450 | 450 | | Arc voltage, V | 23 | 23 | 22 | 25 | 26 | 26 | 26 | | Welding current, A | 50-80 | 70-110 | 110-150 | 110-150 | 150-200 | 190-260 | 0,73 | | N. Kg weld metal/kg electrodes | 0,61 | 0,64 | 0,63 | 0,67 | 0,68 | 0,72 | 9,0 | | B. No. of electrodes/kg weld metal | 125 | 67,0 | 42,3 | 30,0 | 20,0 | 13,0 | 3,80 | | H. Kg weld metal/hour arc time | 0,67 | 1,0 | 1,37 | 1,5 | 2,0 | 2,8 | 113 | | T. Burn-off time, secs/electrode | 44 | 59 | 62,4 | 92 | 101 | 106 | - |
|
|