OK 48.04
SMAW


Welding current, A
AC, DC+(-) OCV 65 V


ClassificationsApprovalsTypical all weld metal compositionTypical properties all weld metal
SFA/AWS A5.1
E7018
EN ISO 2560-A
E 42 4 B 32 H5
ABS 3H5, 3Y
BV3YHH
DB10.039.34
DNV3 YH10
GL3YH10
LR3, 3YH15
PRS3YH10
RS3YHH
SeprosUNA 409819
VdTV00050
CEEN 13479
C0,06
Si0,5
Mn1,1
P0,03
S0,03
Redrying temperature, C
350
Redrying time, hours
2
Recovery
125%
Yield stress, MPa
480
Tensile strength, MPa
560
Elongation, %
30
Elongation, %
30
Charpy V
Test temps, CImpact values, J
-20150
-40100

Diameter, mm2,02,53,23,24,05,06,0
Length, mm 300 350 350 450 450 450 450
Arc voltage, V 23 23 22 25 26 26 26
Welding current, A 50-80 70-110 110-150 110-150 150-200 190-260 0,73
N. Kg weld metal/kg electrodes 0,61 0,64 0,63 0,67 0,68 0,72 9,0
B. No. of electrodes/kg weld metal 125 67,0 42,3 30,0 20,0 13,0 3,80
H. Kg weld metal/hour arc time 0,67 1,0 1,37 1,5 2,0 2,8 113
T. Burn-off time, secs/electrode 44 59 62,4 92 101 106 -

 