OK Tubrod 14.31
FCAW
Type Rutile

A flux-cored tubular wire used for the joining of the 316 low-carbon type 18-20Cr10-14Ni2-3Mo steels. The composition also ensures that the stabilised types may be welded with equal success. Capable of welding in the spray transfer mode, very high deposition rates are assured. The weld appearance is bright, fine and evenly rippled surface finish with minimal spatter. Shielding gas CO2 or Ar+20%CO2.
Welding current, A
DC+


ClassificationsApprovalsTypical all weld metal compositionTypical properties all weld metal
SFA/AWS A5.22
E316LT0-1
SFA/AWS A5.22
E316LT0-4
EN 12073
T 19 12 3 L R M 3
VdTV05147
C0,04
Si0,6
Mn1,4
Cr18,5
Ni12,0
Mo2,7
Cu0,3
Yield stress, MPa
>320
Tensile strength, MPa
>510
Elongation, %
>25
Elongation, %
>25
Charpy V
Test temps, CImpact values, J
+2040
-19632

Diameter, mm1,21,6
Arc voltage, V 25-32 26-34
Welding current, A 150-250 200-350
H. Kg weld metal/hour arc time 2,5-7,0 3,0-7,5
Wire feed, m/min 8,0-16,0 4,0-11,0

 