OK 92.35 SMAW
Welding current, A DC+, AC OCV 70 V
|
|
Classifications | Approvals | Typical all weld metal composition | Typical properties all weld metal | SFA/AWS A5.11 | (ENiCrMo-5) | DIN 8555 | E 23-250 CKT |
| | C | 0,05 | Si | 0,5 | Mn | 0,8 | Cr | 15,5 | Ni | 57 | Mo | 16,4 | W | 3,5 | Fe | 5,5 |
| Redrying temperature, °C 350 Redrying time, hours 2 Recovery 185-190 Yield stress, MPa 515 Tensile strength, MPa 750 Elongation, % 17 Weld metal hardness, a w 240-260 HV Weld metal hardness, w h 40-45 HRC Machinability Fair High temp. wear resistance Excellent Corrosion resistance Very good
|
Diameter, mm | 2,5 | 3,2 | 4,0 | 5,0 | Length, mm | 300 | 350 | 350 | 350 | Arc voltage, V | 18 | 18 | 20 | 20 | Welding current, A | 65-110 | 110-150 | 160-200 | 190-250 | N. Kg weld metal/kg electrodes | 0,61 | 0,63 | 0,64 | 0,65 | B. No. of electrodes/kg weld metal | 56 | 28 | 19 | 11 | H. Kg weld metal/hour arc time | 1,1 | 1,6 | 2,3 | 3,1 | T. Burn-off time, secs/electrode | 62 | 86 | 89 | 106 |
|
|