OK 92.35
SMAW


Welding current, A
DC+, AC OCV 70 V


ClassificationsApprovalsTypical all weld metal compositionTypical properties all weld metal
SFA/AWS A5.11
(ENiCrMo-5)
DIN 8555
E 23-250 CKT
C0,05
Si0,5
Mn0,8
Cr15,5
Ni57
Mo16,4
W3,5
Fe5,5
Redrying temperature, C
350
Redrying time, hours
2
Recovery
185-190
Yield stress, MPa
515
Tensile strength, MPa
750
Elongation, %
17
Weld metal hardness, a w
240-260 HV
Weld metal hardness, w h
40-45 HRC
Machinability
Fair
High temp. wear resistance
Excellent
Corrosion resistance
Very good

Diameter, mm2,53,24,05,0
Length, mm 300 350 350 350
Arc voltage, V 18 18 20 20
Welding current, A 65-110 110-150 160-200 190-250
N. Kg weld metal/kg electrodes 0,61 0,63 0,64 0,65
B. No. of electrodes/kg weld metal 56 28 19 11
H. Kg weld metal/hour arc time 1,1 1,6 2,3 3,1
T. Burn-off time, secs/electrode 62 86 89 106

 