FILARC 88S
SMAW


Welding current, A
DC+/-, AC OCV 65 V


ClassificationsApprovalsTypical all weld metal compositionTypical properties all weld metal
SFA/AWS A5.5
E8016-G
EN ISO 2560-A
E 50 6 Mn1Ni B 12 H5
ABSE8016-G (-60C)
DB10.105.16
DNV3 YH10
GL6YH10
LR5Y40H15
VdTV06107
CEEN 13479
C0,06
Si0,4
Mn1,7
Ni0,8
P0,02
S0,015
Cr0,05
Mo0,01
V0,02
Nb0,01
Cu0,05
Al0,008
Sn0,01
Ti0,03
Pb0,01
As0,02
Sb0,01
Recovery
100%
Yield stress, MPa
>500
Tensile strength, MPa
560-660
Elongation, %
>22
Elongation, %
>22
Charpy V
Test temps, CImpact values, J
-20150
-40100
-6060

Diameter, mm2,53,24,04,05,0
Length, mm 350 350 350 450 450
Arc voltage, V 21,2 21,4 21,0 21,5 22,6
Welding current, A 55-85 80-140 110-170 110-170 180-230
N. Kg weld metal/kg electrodes 0,65 0,59 0,58 0,62 0,63
B. No. of electrodes/kg weld metal 87,1 54,5 36,6 26,8 16,9
H. Kg weld metal/hour arc time 0,7 0,96 1,2 1,27 1,95
T. Burn-off time, secs/electrode 59 69 82 106 109

 