OK 46.16
SMAW


Welding current, A
AC, DC+ - OCV 50 V


ClassificationsApprovalsTypical all weld metal compositionTypical properties all weld metal
SFA/AWS A5.1
E7014
EN ISO 2560-A
E 38 0 RC 11
ABS2
BV2
DB80.039.03
DNV2
GL2
LR2
PRS2
VdTÜV02528
CEEN03479
C0,08
Si0,4
Mn0,5
P³0,03
S³0,03
Redrying temperature, °C
70
Redrying time, hours
1
Recovery
100%
Yield stress, MPa
440
Tensile strength, MPa
505
Elongation, %
28
Elongation, %
28
Charpy V
Test temps, °CImpact values, J
+2075
070
-2040

Diameter, mm2,02,53,24,04,05,06,0
Length, mm 300 350 350 350 450 450 450
Arc voltage, V 24 22 23 24 24 26 26
Welding current, A 50-70 60-100 80-150 100-200 100-200 150-260 200-385
N. Kg weld metal/kg electrodes 0,57 0,58 0,58 0,59 0,61 0,63 0,58
B. No. of electrodes/kg weld metal 167 84,0 52,0 34,0 26,0 17,0 12,0
H. Kg weld metal/hour arc time 0,54 0,7 1,3 1,8 1,8 2,3 3,8
T. Burn-off time, secs/electrode 40 40 59 65 77 105 80

 