OK Autrod 12.51
GMAW

A copper-coated, manganese-silicon bearing electrode for the GMAW of unalloyed steels, such as general structural steels with a minimum tensile strength of 530 MPa, and for fine-grained, carbon-manganese steels with a minimum yield strength of 420 MPa. OK Autrod 12.51 can be welded with Ar/20CO2 or pure CO2 as the shielding gas. The mechanical properties quoted here are welded with Ar/20CO2 as the shielding gas.
Welding current, A
DC(+)


ClassificationsApprovalsTypical all weld metal compositionTypical properties all weld metal
SFA/AWS A5.18
ER70S-6
EN 440
G3Si1
ABS3SA, 3YSA
BVSA3YM
CL 
DB42.039.06
DNVIII YMS
DSEN 440
GL3YS
LR3 3YS
PRS3YS
RINASG 52 3
RS3YMS
SeprosUNA 485178
SFSEN 440
SSEN 440
UDTDIN 8559
42.039/1
VdTV 
C0,1
Si0,9
Mn1,5
Wire composition
Yield stress, MPa
470
Tensile strength, MPa
560
Elongation, %
26
Elongation, %
26
Charpy V
Test temps, CImpact values, J
+20130
-2090
-3070

Diameter, mm0,60,80,91,01,21,41,6
Arc voltage, V 15-20 18-24 18-26 18-32 18-34 22-36 28-38
Welding current, A 30-100 60-200 70-250 80-300 120-380 150-420 225-550
Wire feed, m/min 5,5-13 3,2-13 3,0-12 2,7-15 2,5-15 2,3-12 2,3-12
Deposition rate kg weld metal/hour 0,7-1,7 0,8-3,0 0,9-3,6 1,0-5,6 1,3-8,0 1,6-8,7 2,1-11,4

 