OK Tubrod 14.32
FCAW
Type Rutile

A flux-cored tubular wire depositing weld metal of the 309 type. Apart from joining these steels the weld metal ferrite content ensures that it is suitable for dissimilar applications as well as joining difficult-to-weld steels. Shielding gas CO2 or Ar+20%CO2.
Welding current, A
DC+


ClassificationsApprovalsTypical all weld metal compositionTypical properties all weld metal
SFA/AWS A5.22
E309LT0-1
SFA/AWS A5.22
E309LT0-4
EN 12073
T 23 12 L R M 3
VdTV05149
C0,04
Si0,4
Mn1,1
Cr24,0
Ni13,0
Mo0,3
Cu0,3
Yield stress, MPa
449
Tensile strength, MPa
594
Elongation, %
30
Elongation, %
30
Charpy V
Test temps, CImpact values, J
+2042

Diameter, mm1,21,6
Arc voltage, V 25-32 26-34
Welding current, A 150-250 200-350
H. Kg weld metal/hour arc time 2,5-7,0 3,0-7,5
Wire feed, m/min 8,0-16,0 4,0-11,0

 