OK 92.86
SMAW


Welding current, A
DC+


ClassificationsApprovalsTypical all weld metal compositionTypical properties all weld metal
SFA/AWS A5.11
E NiCu-7
EN ISO 14172
E Ni 4060 (NiCu30Mn3Ti)
C0,01
Si0,3
Mn2,1
Ni66
Nb<0,3
Cu29
Al<0,5
Ti0,2
Fe1,6
Redrying temperature, C
200
Redrying time, hours
2
Recovery
105
Yield stress, MPa
410
Tensile strength, MPa
640
Elongation, %
40
Elongation, %
40
Ferrite content
FN 0
Charpy V
Test temps, CImpact values, J
+20100
-19680

Diameter, mm2,53,24,0
Length, mm 300 350 350
Arc voltage, V 22 26 28
Welding current, A 50-70 70-120 120-140
N. Kg weld metal/kg electrodes 0,63 0,63 0,63
B. No. of electrodes/kg weld metal 83 42 28
H. Kg weld metal/hour arc time 1,0 1,6 2,4
T. Burn-off time, secs/electrode 45 52 54

 