OK 61.35
SMAW
Welding current, A
DC+
|
      |
| Classifications | Approvals | Typical all weld metal composition | Typical properties all weld metal | | EN 1600 | | E 19 9 L B 2 2 | | SFA/AWS A5.4 | | E308L-15 | | Werkstoff Nr. | | 1.4316 |
| | Sepros | UNA 409820 | |
| UDT | EN 1600 | |
| VdTÜV | 04811 | |
| | C | <0,04 | | Si | 0,5 | | Mn | 1,7 | | Cr | 19,0 | | Ni | 10,0 | | Mo | <0,3 | | Cu | <0,3 |
| Redrying temperature, °C
200
Redrying time, hours
2
Recovery
100
Yield stress, MPa
460
Tensile strength, MPa
580
Elongation, %
60
Elongation, %
60
Ferrite content
FN 2-7
| Charpy V | | Test temps, °C | Impact values, J | | +20 | 100 | | -120 | 70 | | -196 | >32 |
|
| Diameter, mm | 2,5 | 3,2 | 4,0 | 5,0 | | Length, mm | 300 | 350 | 350 | 350 | | Arc voltage, V | 22 | 25 | 27 | 26 | | Welding current, A | 55-85 | 80-120 | 80-180 | 160-210 | | N. Kg weld metal/kg electrodes | 0,61 | 0,61 | 0,61 | 0,51 | | B. No. of electrodes/kg weld metal | 92 | 50 | 33 | 25 | | H. Kg weld metal/hour arc time | 0,9 | 1,3 | 1,9 | 2,2 | | T. Burn-off time, secs/electrode | 37 | 54 | 58 | 66 |
|
|