OK 61.35
SMAW


Welding current, A
DC+


ClassificationsApprovalsTypical all weld metal compositionTypical properties all weld metal
EN 1600
E 19 9 L B 2 2
SFA/AWS A5.4
E308L-15
Werkstoff Nr.
1.4316
SeprosUNA 409820
UDTEN 1600
VdTÜV04811
C<0,04
Si0,5
Mn1,7
Cr19,0
Ni10,0
Mo<0,3
Cu<0,3
Redrying temperature, °C
200
Redrying time, hours
2
Recovery
100
Yield stress, MPa
460
Tensile strength, MPa
580
Elongation, %
60
Elongation, %
60
Ferrite content
FN 2-7
Charpy V
Test temps, °CImpact values, J
+20100
-12070
-196>32

Diameter, mm2,53,24,05,0
Length, mm 300 350 350 350
Arc voltage, V 22 25 27 26
Welding current, A 55-85 80-120 80-180 160-210
N. Kg weld metal/kg electrodes 0,61 0,61 0,61 0,51
B. No. of electrodes/kg weld metal 92 50 33 25
H. Kg weld metal/hour arc time 0,9 1,3 1,9 2,2
T. Burn-off time, secs/electrode 37 54 58 66

 