OK 53.35
SMAW
Welding current, A
AC, DC+ OCV 65 V
|
      |
| Classifications | Approvals | Typical all weld metal composition | Typical properties all weld metal | | SFA/AWS A5.1 | | E7048 | | CSN 05 5010 | | E 51.93 | | DIN 1913 | | E 51 54 B9 | | EN ISO 2560-A | | E 42 4 B 31 H5 | | ISO 2560 | | E 51 5B 56H |
| | ABS | 3H5, 3Y | |
| BV | 3 YHH | |
| DB | 10.039.33 | |
| DNV | 3 YH10 | |
| DS | EN 499 | |
| GL | 3YH10 | |
| LR | 3, 3Y H15 | |
| PRS | 3 YH10 | |
| RS | 3YHH | |
| SFS | EN 499 | |
| SS | EN 499 | |
| Ü | 10.039/1 | |
| VdTÜV | 00631 | |
| CE | EN 13479 | |
| | C | 0,06 | | Si | 0,5 | | Mn | 0,9 | | P | ³0,03 | | S | ³0,03 |
| Redrying temperature, °C
350
Redrying time, hours
2
Recovery
105%
Yield stress, MPa
460
Tensile strength, MPa
560
Elongation, %
30
Elongation, %
30
| Charpy V | | Test temps, °C | Impact values, J | | -20 | 140 | | -30 | 110 | | -40 | 90 |
|
| Diameter, mm | 3,2 | 4,0 | 4,5 | 5,0 | | Length, mm | 450 | 450 | 450 | 450 | | Arc voltage, V | 25 | 27 | 27 | 28 | | Welding current, A | 80-150 | 110-200 | 150-230 | 170-280 | | N. Kg weld metal/kg electrodes | 0,65 | 0,70 | 0,64 | 0,68 | | B. No. of electrodes/kg weld metal | 38 | 25,0 | 20 | 16,0 | | H. Kg weld metal/hour arc time | 1,37 | 2,2 | 2 | 2,9 | | T. Burn-off time, secs/electrode | 69 | 69 | 89 | 77 |
|
|