FILARC 118
SMAW
Welding current, A
DC+/-, AC OCV 65 V
|
      |
| Classifications | Approvals | Typical all weld metal composition | Typical properties all weld metal | | SFA/AWS A5.5 | | E11018-M | | EN 757 | | E 69 5 Mn2NiMo B 32 H5 |
| | ABS | E11018-M | |
| BV | 4Y62H5 | |
| DNV | 4 Y62H10 | |
| LR | 4Y62H5 | |
| MoD | (N) Q1N, HY80 | |
| CE | EN13479 | |
| | CR | ³0,07 | | Si | 0,4 | | Mn | 1,6 | | Ni | 2,2 | | Mo | 0,4 | | P | ³0,02 | | S | ³0,02 | | Cr | ³0,07 | | V | ³0,02 | | Nb | ³0,01 | | Cu | ³0,05 | | Al | 0,008 | | Sn | ³0,01 | | Ti | ³0,03 | | Pb | ³0,01 | | As | ³0,02 |
| Recovery
120%
Yield stress, MPa
<760
Tensile strength, MPa
>760
Elongation, %
>20
Elongation, %
>20
| Charpy V | | Test temps, °C | Impact values, J | | -51 | >47 |
|
| Diameter, mm | 2,5 | 3,2 | 4,0 | 5,0 | | Length, mm | 350 | 350 | 450 | 450 | | Arc voltage, V | 25,3 | 22,8 | 22,8 | 24,6 | | Welding current, A | 55-105 | 90-140 | 110-180 | 190-280 | | N. Kg weld metal/kg electrodes | 0,61 | 0,56 | 0,61 | 0,63 | | B. No. of electrodes/kg weld metal | 83,3 | 46,2 | 23,1 | 13,5 | | H. Kg weld metal/hour arc time | 0,93 | 1,21 | 1,72 | 2,75 | | T. Burn-off time, secs/electrode | 46,6 | 64,3 | 90,0 | 90,3 |
|
|