FILARC 118
SMAW


Welding current, A
DC+/-, AC OCV 65 V


ClassificationsApprovalsTypical all weld metal compositionTypical properties all weld metal
SFA/AWS A5.5
E11018-M
EN 757
E 69 5 Mn2NiMo B 32 H5
ABSE11018-M
BV4Y62H5
DNV4 Y62H10
LR4Y62H5
MoD(N) Q1N, HY80
CEEN13479
CR0,07
Si0,4
Mn1,6
Ni2,2
Mo0,4
P0,02
S0,02
Cr0,07
V0,02
Nb0,01
Cu0,05
Al0,008
Sn0,01
Ti0,03
Pb0,01
As0,02
Recovery
120%
Yield stress, MPa
<760
Tensile strength, MPa
>760
Elongation, %
>20
Elongation, %
>20
Charpy V
Test temps, CImpact values, J
-51>47

Diameter, mm2,53,24,05,0
Length, mm 350 350 450 450
Arc voltage, V 25,3 22,8 22,8 24,6
Welding current, A 55-105 90-140 110-180 190-280
N. Kg weld metal/kg electrodes 0,61 0,56 0,61 0,63
B. No. of electrodes/kg weld metal 83,3 46,2 23,1 13,5
H. Kg weld metal/hour arc time 0,93 1,21 1,72 2,75
T. Burn-off time, secs/electrode 46,6 64,3 90,0 90,3

 