OK 92.60
SMAW
Type Basic

An electrode of the nickel-iron type for welding normal grades of cast iron and for joining them to steel. The electrode has very good current-carrying capacity. The electrode produces a weld metal stronger and more resistant to solidification cracking than that of the nickel electrode type.
Welding current, A
AC, DC+ OCV 45 V


ClassificationsApprovalsTypical all weld metal compositionTypical properties all weld metal
SFA/AWS A5.15
ENiFe-CI
EN ISO 1071
E C NiFe-1 3
SeprosUNA 409820
C0,9
Si<0,8
Mn0,7
Ni52
Nb0,2
Cu1,0
Al0,3
Fe44
Redrying temperature, °C
200
Redrying time, hours
2
Recovery
110
Yield stress, MPa
380
Tensile strength, MPa
560
Elongation, %
>15
Elongation, %
>15
Weld metal hardness, a w
200 HB
Machinability
Good

Diameter, mm2,53,24,05,0
Length, mm 300 350 350 350
Arc voltage, V 22 23 23 23
Welding current, A 60-100 80-150 100-200 150-250
N. Kg weld metal/kg electrodes 0,70 0,70 0,70 0,70
B. No. of electrodes/kg weld metal 85 44 30 19
H. Kg weld metal/hour arc time 0,8 1,2 1,6 2,4
T. Burn-off time, secs/electrode 45 56 59 66

 